Magnesia-Zirconia Brick for Glass Kiln Regenerators
Custom-engineered for glass furnace regenerators, our magnesia-zirconia brick blends high-purity magnesite and zirconia via advanced sintering. It integrates magnesia’s alkali resistance and zirconia’s thermal stability, tailored to the harsh cyclic high-temperature, alkaline erosion environment of glass kiln regenerators, serving as a premium refractory for glass manufacturing.
Core Advantages
Superior Thermal Shock Resistance
ZrO₂-modified structure enhances resistance to rapid temperature changes, perfectly adapting to glass furnace regenerators’ frequent heating-cooling cycles, effectively preventing cracking, peeling and structural damage.
Strong Alkali & Erosion Resistance
High MgO content resists alkaline glass melts, flue gas and dust erosion, while zirconia reinforces surface compactness, outperforming ordinary magnesia bricks in glass kiln harsh working conditions.
Excellent High-Temperature Stability
Withstands high temperatures , maintaining structural density, mechanical strength and dimensional stability under prolonged high-temperature operation in regenerators.
Energy-Saving & Long Lifespan
Dense texture minimizes heat loss, improves heat storage and exchange efficiency of regenerators, reduces glass furnace energy consumption, and extends lining service life to lower maintenance costs.
Product Parameters
| Item | Magnesia-Chrome Bricks | Magnesia-Zirconia Bricks | ||||
| DMC-20 | DMC-16 | DMC-12 | DMC-8 | MZr-75 | MZr-78 | |
| MgO % | 55 | 60 | 65 | 70 | 75 | 78 |
| SiO₂ % | 1.5 | 1.5 | 2.8 | 3.0 | 10.0 | 8.0 |
| CaO % | / | / | / | / | 2.0 | 1.5 |
| ZrO₂ % | / | / | / | / | 13.0 | 13.0 |
| Cr₂O₃ % | 20 | 16 | 12 | 8 | 2.0 | 3.0 |
| g/cm³ Bulk Density |
3.15 | 3.05 | 3.02 | 2.95 | 3.10 | 3.18 |
| % Apparent Porosity |
16 | 16 | 18 | 18 | 15 | 14 |
| MPa Cold Crushing Strength |
40 | 40 | 40 | 40 | 80 | 100 |
| ℃（0.2MPa,0.6%） Refractoriness Under Load |
1700 | 1700 | 1650 | 1620 | 1600 | 1670 |
| Thermal shock stability （950℃ cooling)times | 20 | 20 | 20 | 20 | 15 | 15 |
Detailed Application Scenarios
1. Application Scenarios
◎ This magnesia-zirconia brick is exclusively designed for glass furnace regenerators, widely applicable to float glass, container glass, optical glass, borosilicate glass and other specialty glass production lines. It is specifically suitable for lining key parts of glass furnace regenerators, including checkerwork (grid bricks), upper chamber linings (high-temperature zone in contact with flue gas), lower chamber linings (thermal exchange zone), flue connections (transition zone with temperature fluctuations), and regenerator throat parts (high erosion area). It perfectly adapts to the core working conditions of glass furnace regenerators, such as cyclic heating-cooling (temperature difference up to 800℃), alkaline erosion from glass melt volatiles and flue dust, and thermal shock caused by air-fuel switching, ensuring stable operation of the regenerator and improving the overall efficiency of the glass furnace.